Mianly Spes nke6082 Aluminom Alloy
N'ụdị efere, 6082 bụ alloy a na-ejikarị eme ihe maka nhazi izugbe. A na-ejikarị ya eme ihe na Europe ma dochie 6061 alloy n'ọtụtụ ngwa, nke bụ isi n'ihi ike ya dị elu (site na nnukwu manganese) na nguzogide ya dị mma na corrosion. A na-ahụkarị ya na njem njem, ihe nlegharị anya, àkwà mmiri na injinịa izugbe.
Ihe mejupụtara kemịkalụ WT(%) | |||||||||
Silikoni | Ígwè | Ọla kọpa | Magnesium | Manganese | Chromium | Zinc | Titanium | Ndị ọzọ | Aluminom |
0.7-1.3 | 0.5 | 0.1 | 0.6-1.2 | 0.4-1.0 | 0.25 | 0.2 | 0.1 | 0.15 | Nhazi |
Ụdị iwe ọkụ
Ihe na-ewekarị iwe maka 6082 alloy bụ:
F - Dị ka e mepụtara.
T5 - Ajụjụ site na usoro nhazi ọnọdụ okpomọkụ dị elu yana ịka nká. Na-emetụta ngwaahịa ndị na-adịghị oyi na-arụ ọrụ mgbe jụrụ oyi.
T5511 - jụrụ oyi site na usoro nhazi okpomọkụ dị elu, na-ebelata nrụgide site na ịgbatị na ịka nká.
T6 - Ngwọta okpomọkụ na-agwọta ma mee agadi.
O - Annealed. Nke a bụ ike kacha nta, iwe ọkụ ductility kacha elu.
T4 - ọgwụgwọ okpomọkụ na-agwọta ma mee agadi ka ọ bụrụ ọnọdụ kwụsiri ike. Na-emetụta ngwaahịa na-adịghị oyi na-arụ ọrụ mgbe ngwọta okpomọkụ-ọgwụgwọ.
T6511 - Ngwọta ọgwụgwọ ọgwụgwọ, nchekasị na-ebelata site na ịgbatị, na ịka nká.
Njirimara arụrụ arụ | ||||
Iwe | Ọkpụrụkpụ (mm) | Ike ọdụdọ (Mpa) | Mpụta Ike (Mpa) | Ogologo oge (%) |
T4 | 0.4-1.50 | ≥205 | ≥110 | ≥12 |
T4 | 1.50-3.00 | ≥14 | ||
T4 | 3.00-6.00 | ≥15 | ||
T4 | 6.00-12.50 | ≥14 | ||
T4 | 12.50-40.00 | ≥13 | ||
T4 | 40.00-80.00 | ≥12 | ||
T6 | 0.4-1.50 | ≥310 | ≥260 | ≥6 |
T6 | 1.50-3.00 | ≥7 | ||
T6 | 3.00-6.00 | ≥10 | ||
T6 | 6.00-12.50 | ≥300 | ≥255 | ≥9 |
Alloy 6082 Njirimara
Alloy 6082 na-enye ihe ndị yiri ya, ma ọ bụghị otu, njirimara anụ ahụ na 6061 alloy, yana ihe ndị dị elu dị elu na ọnọdụ -T6. Ọ nwere njirimara njedebe dị mma ma na-anabata nke ọma na mkpuchi anodic ndị a na-ahụkarị (ya bụ, doro anya, doro anya na agba, akwa akwa).
Enwere ike itinye usoro njikọta azụmahịa dị iche iche (dịka ọmụmaatụ, ịgbado ọkụ, brazing, wdg) na alloy 6082; Otú ọ dị, ọgwụgwọ okpomọkụ nwere ike ibelata ike na mpaghara weld. Ọ na-enye ezigbo igwe na -T5 na -T6 iwe, mana a na-atụ aro mgbawa mgbawa ma ọ bụ usoro igwe pụrụ iche (dịka ọmụmaatụ, mkpọpu peck) maka ịkwalite nhazi mgbawa.
A na-atụ aro iwe -0 ma ọ bụ -T4 mgbe ọ na-ehulata ma ọ bụ na-akpụ alloy 6082. Ọ pụkwara isi ike ịmepụta ụdị extrusion dị mkpa na 6082 alloy, ya mere -T6 iwe nwere ike ọ gaghị adị n'ihi njedebe nkwụsịtụ alloy.
Na-eji maka 6082 Alloy
Alloy 6082 dị mma weldability, brazeability, corrosion resistance, formability na machinability na-eme ka ọ baa uru maka mkpanaka, mmanya na ngwaahịa machining, tubing aluminum na-enweghị ntụpọ, profaịlụ nhazi na profaịlụ omenala.
Àgwà ndị a, yana ịdị arọ ya na ihe ndị dị mma na-arụ ọrụ, nyere aka na iji 6082-T6 alloy na ụgbọ ala, ụgbọ elu na ngwa ụgbọ okporo ígwè dị elu.