100% Original Aluminum 6061 - 4043 Aluminum Plate – Miandi
100% Original Aluminum 6061 - 4043 Aluminum Plate – Miandi Detail:
4043 Aluminum Alloy with high shear strength and heat resistance. It is very beneficial to avoid welding cracks, this material specially used as a welding material.
|
Chemical Composition WT(%) |
|||||||||
|
Silicon |
Iron |
Copper |
Magnesium |
Manganese |
Chromium |
Zinc |
Titanium |
Others |
Aluminum |
|
4.5~6.0 |
0.8 |
0.3 |
0.05 |
0.05 |
- |
0.1 |
0.2 |
0.15 |
Balance |
|
Typical Mechanical Properties |
|||
|
Thickness (mm) |
Tensile Strength (Mpa) |
Yield Strength (Mpa) |
Elongation (%) |
|
0.5~250 |
≥274 |
- |
- |
Applications
Welding Material
Our Advantage
Inventory and Delivery
We have enough product in stock, we can offer enough material to customers. The lead time can be within 7 days for stock materil.
Quality
All the product are from the biggest manufacturer, we can offer the MTC to you. And we can also offer Third-Party test report.
Custom
We have cutting machine, custom size are available.
Product detail pictures:
Related Product Guide:
BC takes Alberta to court – Canada News | A7075 Aluminum Sheet
Acura offers luxury value in ILX | Cars | Aluminium Square Rod
Our commission is always to provide our customers and clientele with best quality and aggressive portable digital products for 100% Original Aluminum 6061 - 4043 Aluminum Plate – Miandi , The product will supply to all over the world, such as: Madras, Pakistan, Paris, Strict quality control is executed in each link of the whole production process.We sincerely hope to establish the friendly and mutual-beneficial cooperation with you. Based on high quality products and perfect pre-sales /after-sales service is our idea, some clients had cooperated with us for more than 5 years.
By Coral from Frankfurt - 2018.11.22 12:28
The company can think what our think, the urgency of urgency to act in the interests of our position, can be said this is a responsible company, we had a happy cooperation!
By Michelle from Tunisia - 2018.11.28 16:25